We report on THz emission in single-crystalline SnS2 in response to above bandgap excitation. Symmetry properties of THz generation suggest that its origin is an ultrafast surface shift current, a 2nd order nonlinear effect that can occur as a result of above-gap photoexcitation of a non-centrosymmetric semiconductor. Multilayer SnS2 can exist in several polytypes that differ in the layer stacking. Of those polytypes, 2H and 18R are centrosymmetric while 4H is not. While Raman spectroscopy suggests that the single crystalline SnS2 in our experiments is 2H, its THz emission has symmetry that are fully consistent with the P3m1 phase of 4H polytype. We hypothesize that the stacking disorder, where strain-free stacking faults that interrupt regions of 2H polytype, can break inversion symmetry and result in THz emission. These results lay the foundations for application of SnS2 as an efficient, stable, flexible THz source material, and highlight the use of THz spectroscopy as a sensitive tool for establishing symmetry properties of materials. 

Abstract Significant optical absorption in the blue–green spectral range, high intralayer carrier mobility, and band alignment suitable for water splitting suggest tin disulfide (SnS₂) as a candidate material for photo‐electrochemical applications. In this work, vertically aligned SnS₂nanoflakes are synthesized directly on transparent conductive substrates using a scalable close space sublimation (CSS) method. Detailed characterization by time‐resolved terahertz and time‐resolved photoluminescence spectroscopies reveals a high intrinsic carrier mobility of 330 cm²V⁻¹s⁻¹and photoexcited carrier lifetimes of 1.3 ns in these nanoflakes, resulting in a long vertical diffusion length of ≈1 µm. The highest photo‐electrochemical performance is achieved by growing SnS₂nanoflakes with heights that are between this diffusion length and the optical absorption depth of ≈2 µm, which balances the competing requirements of charge transport and light absorption. Moreover, the unique stepped morphology of these CSS‐grown nanoflakes improves photocurrent by exposing multiple edge sites in every nanoflake. The optimized vertical SnS₂nanoflake photoanodes produce record photocurrents of 4.5 mA cm⁻²for oxidation of a sulfite hole scavenger and 2.6 mA cm⁻²for water oxidation without any hole scavenger, both at 1.23 V_RHEin neutral electrolyte under simulated AM1.5G sunlight, and stable photocurrents for iodide oxidation in acidic electrolyte.